Product
Autolad2GH
Characteristic
- CTI≥600V for hash environment and critical design for safe creepage distance
- Excellent high voltage anti-CAF
- Robust thermal cycling resistance
- Halogen, antimony and red phosphorous free
Application Area
- High power & high voltage applications
- EV automotive electrification
- On board charger (OBC), etc.
- Product Performance
- Product Certificate
- Data Download
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 190 |
| 2.4.25D |
DSC |
175 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 402 |
|
T288 |
2.4.24.1 | TMA | min | >60 |
| T260 |
2.4.24.1 |
TMA |
min |
>60 |
|
Thermal Stress |
2.4.13.1 |
288℃, solder dip |
- |
>100s No Delamination |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 35 |
| After Tg | ppm/℃ | 190 | ||
| 50-260℃ | % | 2.1 | ||
| Dissipation Constant (1GHz) | 2.5.5.9 | C-24/23/50 | - | 4.3 |
|
Dissipation Factor (1GHz) |
2.5.5.9 |
C-24/23/50 |
- | 0.015 |
| Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ.cm | 4.83×107 |
|
Surface Resistivity |
2.5.17.1 |
C-96/35/90 | MΩ | 4.98×106 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 130 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.2 [6.86] |
| Flexural Strength (LW/CW) | 2.4.4 | A | MPa | 520/400 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.09 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC0(≥600V) |
Remarks:
Remark:
1. Specification sheet: IPC-4101/130, is for your reference only.
2. All the typical value is based on the 1.6mm (8X7628) specimen, “ * ” is based on the 1.0mm(9X2116) specimen.
3. In order to satisfy CTI≥600V, 2116(RC≥54%)，7628(RC≥45%) or above thickness prepreg is suggested to be used for outer prepreg layer.
4. All the typical value listed above is for your reference only, please turn to Shengyi Technology Co., Ltd for detailed information, and all rights from this data sheet are reserved by Shengyi Technology Co., Ltd.